Items related to Structural characterization and analysis of Sr2SiO4...
Synopsis
Strontium silicate (Sr2SiO4) nanophosphors were prepared by solution combustion synthesis method were characterised by X-ray diffraction, SEM and TEM. Structural optimisation of Sr2SiO4 nanophosphors were done by variation in temperature, fuel and calcination temperature and for the synthesis was obtained. The optimal condition for phosphor synthesised using glycine as a fuel calcinated at 900° C for the duration of 3 hours exhibited better crystallinity. The optimal condition was used further in synthesising of Sr2SiO4: Sm3+, Sr2SiO4: Eu3+ and Sr2SiO4: Dy3+ phosphors. XRD of all the synthesised phosphors were well indexed with JCPDS card No.39-1256 that corresponds to orthorhombic structure. Scherrer and WH-plots were used to determine the average crystallite size and were found to be around 40 nm, 43 nm and 38 nm for Sm3+, Eu3+ and Dy3+ doped Sr2SiO4 respectively. Detailed structural analysis of Dy3+ doped Sr2SiO4 was studied.
"synopsis" may belong to another edition of this title.
Buy New
View this item
US$ 53.01
US$ 26.96 shipping from Germany to U.S.A.
Destination, rates & speedsSearch results for Structural characterization and analysis of Sr2SiO4...
Stock Image
Structural characterization and analysis of Sr2SiO4 Nanophosphors
Published by
LAP LAMBERT Academic Publishing Jan 2024, 2024
ISBN 10: 6207460014
ISBN 13: 9786207460014
New
Taschenbuch
Seller: BuchWeltWeit Ludwig Meier e.K., Bergisch Gladbach, Germany
Seller rating 5 out of 5 stars
Taschenbuch. Condition: Neu. This item is printed on demand - it takes 3-4 days longer - Neuware 68 pp. Englisch. Seller Inventory # 9786207460014
Quantity: 2 available
Seller Image
Structural characterization and analysis of Sr2SiO4 Nanophosphors : Exploring the Structural Properties of Sr2SiO4 Nanophosphors: A Comprehensive Investigation
Published by
LAP LAMBERT Academic Publishing
ISBN 10: 6207460014
ISBN 13: 9786207460014
New
Taschenbuch
Seller: AHA-BUCH GmbH, Einbeck, Germany
Seller rating 5 out of 5 stars
Taschenbuch. Condition: Neu. nach der Bestellung gedruckt Neuware - Printed after ordering - Strontium silicate (Sr2SiO4) nanophosphors were prepared by solution combustion synthesis method were characterised by X-ray diffraction, SEM and TEM. Structural optimisation of Sr2SiO4 nanophosphors were done by variation in temperature, fuel and calcination temperature and for the synthesis was obtained. The optimal condition for phosphor synthesised using glycine as a fuel calcinated at 900° C for the duration of 3 hours exhibited better crystallinity. The optimal condition was used further in synthesising of Sr2SiO4:Sm3+, Sr2SiO4:Eu3+ and Sr2SiO4:Dy3+ phosphors. XRD of all the synthesised phosphors were well indexed with JCPDS card No.39-1256 that corresponds to orthorhombic structure. Scherrer and WH-plots were used to determine the average crystallite size and were found to be around 40 nm, 43 nm and 38 nm for Sm3+, Eu3+ and Dy3+ doped Sr2SiO4 respectively. Detailed structural analysis of Dy3+ doped Sr2SiO4 was studied. Seller Inventory # 9786207460014
Quantity: 1 available
Seller Image
Structural characterization and analysis of Sr2SiO4 Nanophosphors
Published by
LAP Lambert Academic Publishing
ISBN 10: 6207460014
ISBN 13: 9786207460014
New
Softcover
Seller: moluna, Greven, Germany
Seller rating 5 out of 5 stars
Condition: New. Dieser Artikel ist ein Print on Demand Artikel und wird nach Ihrer Bestellung fuer Sie gedruckt. Strontium silicate (Sr2SiO4) nanophosphors were prepared by solution combustion synthesis method were characterised by X-ray diffraction, SEM and TEM. Structural optimisation of Sr2SiO4 nanophosphors were done by variation in temperature, fuel and calcinati. Seller Inventory # 1396902957
Quantity: Over 20 available
Seller Image
Structural characterization and analysis of Sr2SiO4 Nanophosphors
Published by
LAP LAMBERT Academic Publishing Jan 2024, 2024
ISBN 10: 6207460014
ISBN 13: 9786207460014
New
Taschenbuch
Seller: buchversandmimpf2000, Emtmannsberg, BAYE, Germany
Seller rating 5 out of 5 stars
Taschenbuch. Condition: Neu. Neuware -Strontium silicate (Sr2SiO4) nanophosphors were prepared by solution combustion synthesis method were characterised by X-ray diffraction, SEM and TEM. Structural optimisation of Sr2SiO4 nanophosphors were done by variation in temperature, fuel and calcination temperature and for the synthesis was obtained. The optimal condition for phosphor synthesised using glycine as a fuel calcinated at 900° C for the duration of 3 hours exhibited better crystallinity. The optimal condition was used further in synthesising of Sr2SiO4:Sm3+, Sr2SiO4:Eu3+ and Sr2SiO4:Dy3+ phosphors. XRD of all the synthesised phosphors were well indexed with JCPDS card No.39-1256 that corresponds to orthorhombic structure. Scherrer and WH-plots were used to determine the average crystallite size and were found to be around 40 nm, 43 nm and 38 nm for Sm3+, Eu3+ and Dy3+ doped Sr2SiO4 respectively. Detailed structural analysis of Dy3+ doped Sr2SiO4 was studied.Books on Demand GmbH, Überseering 33, 22297 Hamburg 68 pp. Englisch. Seller Inventory # 9786207460014
Quantity: 2 available
Stock Image
Structural characterization and analysis of Sr2SiO4 Nanophosphors
Published by
LAP Lambert Academic Publishing, 2024
ISBN 10: 6207460014
ISBN 13: 9786207460014
New
paperback
Seller: Mispah books, Redhill, SURRE, United Kingdom
Seller rating 4 out of 5 stars
paperback. Condition: New. New. book. Seller Inventory # ERICA80062074600146
Quantity: 1 available